断裂伸长率 : 200%,拉伸强度 : 31MPa,密度 : 0.9g/cm3,熔体流动速率 : 2.8g/10min,用途级别 : 薄膜级,规格级别 : 薄膜,缺口冲击强度 : 2.7,加工级别 : 注塑级,特性级别 : 增强级,用途:BOPP膜，柔性包装 (更多..)

Baypreg F 200 system is a two component polyurethane system used in compression molding of fiber-reinforced sandwich panels to produce a variety of automotive parts. Some identified applications include door panels, sunshades, spare tire covers, load floors, etc. The Baypreg F 200 system provides lightweight alternatives to ABS, PP, SMC, and wood products while demonstrating very high flexural stiffness and excellent thermal properties. Baypreg F 200 system offers very diverse properties over a wide range of part thicknesses and densities while still providing cost effective substrate parts when combined with reinforcing materials. As with any product, use of the Baypreg F 200 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. (更多..)

Nylon 66 reinforced by 20 weight percent long glass
fibers. The pellets are cylindrical and normally as well as the
embedded fibers 10 mm long.

Parts molded of CELSTRAN have outstanding mechanical properties such
as high strength and stiffness combined with high heat deflection.
The notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. The long
fiber reinforcement reduces creep significantly.

The very isotropic shrinkage in the molded parts minimizes the
warpage.

Complex parts can be manufactured with high reproducibility by
injection molding.

Can be used for substituting die cast metal with the advantage of
Weight reduction, no corrosion problems, no post treatment. (更多..)