密度 | 1.16g/cm3 | 熔体流动速率 | 160g/10min | 吸水率 | 0.3% |
缺口冲击强度 | 12 | 成型收缩率 | 0.55% |
|
产品简述
密度 | 1.16g/cm3 | 熔体流动速率 | 160g/10min | 吸水率 | 0.3% |
缺口冲击强度 | 12 | 成型收缩率 | 0.55% |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
物理性能 | 比重 | ASTM D-792 | 1.16 | |||
吸水性 | ASTM D-570 | 0.3 | % | |||
熔体流动速率 | 200℃ 21.6kg | ASTM D-1238 | 160 | g/10min | ||
模塑收缩率 | ASTM D-955 | 0.4-0.7 | % | |||
机械性能 | 拉伸强度 | ASTM D-638 | 430 | kg/cm2 | ||
弯曲模量 | ASTM D-790 | 23000 | kg/cm2 | |||
洛氏硬度 | ASTM D-785 | 102 | R | |||
缺口冲击强度 | 厚度6.4mm 缺口 | ASTM D-256 | 12.0 | kg.cm/cm | ||
弯曲强度 | ASTM D-790 | 650 | kg/cm2 | |||
伸长率 | ASTM D-638 | 50 | % | |||
电气性能 | 绝缘强度 | ASTM D-149 | 540↑ | v/mil | ||
体积电阻率 | ASTM D-257 | 1016↑ | Ω.cm | |||
介电常数 | ASTM D-150 | 2.8↓ | 107Cvl/s | |||
热性能 | 热变形温度 | 未退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 77 | ℃ |
退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 88 | ℃ | ||
维卡软化点 | ASTM D-1525 | 92 | ℃ |