拉伸强度 | 46MPa | 密度 | 1.16g/cm3 | 熔体流动速率 | 6g/10min |
吸水率 | 0.3% | 成型收缩率 | 0.55% |
|
产品简述
拉伸强度 | 46MPa | 密度 | 1.16g/cm3 | 熔体流动速率 | 6g/10min |
吸水率 | 0.3% | 成型收缩率 | 0.55% |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
物理性能 | 吸水率 | ASTM D-570 | 0.3 | % | ||
成型收缩率 | ASTM D-955 | 0.4-0.7 | % | |||
防燃性 | 1/16inch(1.6mm) | UL-94 | V-0 | CLASS | ||
防燃性 | 1/8inch(3.2mm) | UL-94 | V-0 | CLASS | ||
熔体流动速率 | 200℃ 21.6kg | 锦湖方法 | 120 | g/10min | ||
熔体流动速率 | 200℃ 5kg | ASTM D-1238 | 6 | g/10min | ||
比重 | ASTM D-792 | 1.16 | 23/23℃ | |||
机械性能 | 伸长率 | ASTM D-638 | 40 | % | ||
拉伸强度 | 23℃ | ASTM D-638 | 470(6680) | kg/cm2(psi) | ||
弯曲模量 | 23℃ | ASTM D-790 | 23000(327000) | kg/cm2(psi) | ||
洛氏硬度 | ASTM D-785 | 105 | R | |||
弯曲强度 | 23℃ | ASTM D-790 | 680(9670) | kg/cm2(psi) | ||
电气性能 | 诱电率 | ASTM D-150 | 2.8↓ | 106cyl/s | ||
耐电压 | ASTM D-149 | 540↑ | v/mil | |||
体积电阻率 | ASTM D-257 | 1016↑ | Ω.cm | |||
热性能 | 维卡软化点 | ASTM D-1525 | 93(199) | ℃(℉) | ||
热变形温度 | 未退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 78(172) | ℃(℉) | |
退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 87(189) | ℃(℉) |