拉伸强度 | 63MPa | 密度 | 1.07g/cm3 | 熔体流动速率 | 4g/10min |
缺口冲击强度 | 2 | 成型收缩率 | 0.4% |
|
产品简述
拉伸强度 | 63MPa | 密度 | 1.07g/cm3 | 熔体流动速率 | 4g/10min |
缺口冲击强度 | 2 | 成型收缩率 | 0.4% |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 流动系数 | 220℃/5kg | ASTM D-1238 | 4.0 | g/10min |
流动系数 | 220℃/10kg | ASTM D-1238 | 40 | g/10min | |
变缩性 | ASTM D-955 | 0.2~0.6 | % | ||
比重 | ASTM D-792 | 1.07 | |||
机械性能 | IZOD冲击强度 | Notched1/8" | ASTM D-256 | 2.0 | kg·cm/cm |
伸长率 | ASTM D638 | 5 | % | ||
IZOD冲击强度 | Notched1/4" | ASTM D-256 | 1.5 | kg·cm/cm | |
拉伸强度 | ASTM D-638 | 650 | kg/cm2 | ||
弯曲强度 | ASTM D-790 | 1200 | kg/cm2 | ||
洛氏硬度 | R-Scale | ASTM D-785 | 122 | ||
热性能 | 燃烧性 | 1/8" | IEC707 | FH3-25 | mm/min |
燃烧性 | 1/12" | UL-94 | - | ||
维卡软化点 | 1,000g | ASTM D-1525 | 107 | ℃ | |
燃烧性 | 1/16" | UL-94 | HB | ||
热变形温度 | Unannealed 18.5kg/cm21/2" | ASTM D-648 | 89 | ℃ | |
燃烧性 | 1/16" | IEC707 | - | mm/min | |
燃烧性 | 1/8" | UL-94 | HB |