断裂伸长率 | 630% | 密度 | 0.935g/cm3 | 维卡软化点 | 75℃ |
硬度 | 92 | 用途级别 | 薄膜级 | 规格级别 | 吹塑 |
填充物含量 | 14% | 加工级别 | 吹塑级 |
|
产品简述
断裂伸长率 | 630% | 密度 | 0.935g/cm3 | 维卡软化点 | 75℃ |
硬度 | 92 | 用途级别 | 薄膜级 | 规格级别 | 吹塑 |
填充物含量 | 14% | 加工级别 | 吹塑级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.935 | g/cm3 | ||
MFI | ASTM D-1238 | 0.3 | g/10 | |||
物理性能 | 光泽度 | ASTM D-1003A | 79 | % | ||
雾度 | ASTM D-2457 | 2 | % | |||
VA含量 | ISC.DIS 8965/1989(E) | 14 | % | |||
膜厚 | 40 | u | ||||
机械性能 | 落花流水标冲击强度 | ASTM D-1709 A-B | 大于等于300 | g | ||
1%断裂割线模量度 | MD | ASTM D-882B | 58 | N/mm2 | ||
TD | ASTM D-882B | 60 | N/mm2 | |||
拉伸断裂强度 | MD | ASTM D-638 | 27 | N/mm2 | ||
TD | ASTM D-638 | 28 | N/mm2 | |||
拉伸断裂伸长率 | MD | ASTM D-6398 | 530 | % | ||
TD | ASTM D-6398 | 630 | % | |||
撕裂强度 | MD | ASTM D-1922 | 240 | g | ||
TD | ASTM D-1922 | 350 | g | |||
拉伸屈服强度 | MD | ASTM D-638 | 4.9 | N/mm2 | ||
TD | ASTM D-638 | 4.9 | N/mm2 | |||
邵氏硬度 | A | ASTM D-2240 | 92 | |||
D | ASTM D-2240 | 33 | ||||
电气性能 | 介电强度 | ASTM D-149 | 670 | KV/cm | ||
介电常数 | 2×106HZ | ASTM D-150 | 2.9 | |||
热性能 | 熔点 | 95 | °C | |||
维卡软化点 | ASTM D-1525 | 75 | °C |