性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 熔流率 | 190°C/2.16 kg | ASTM D1238 | 0.40 |
g/10 min
|
醋酸乙烯含量 | ExxonMobil Method | 12.8 |
wt%
|
||
机械性能 | 割线模量 | 1% 正割, MD | ASTM D882 | 80.4 |
MPa
|
1% 正割, TD | ASTM D882 | 89.9 |
MPa
|
||
抗张强度 |
MD: 断裂
|
ASTM D882 | 33.9 |
MPa
|
|
TD: 断裂
|
ASTM D882 | 34.6 |
MPa
|
||
伸长率 |
MD: 断裂
|
ASTM D882 | 360 |
%
|
|
TD: 断裂
|
ASTM D882 | 660 |
%
|
||
落锤冲击 | ASTM D1709A | 710 | g | ||
埃尔曼多夫抗撕强度 |
MD
|
ASTM D1922 | 66 | g | |
TD
|
ASTM D1922 | 82 | g | ||
热性能 | 维卡软化温度 | ASTM D1525 | 76.0 |
°C
|