性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 熔流率 | 190°C/2.16 kg | ASTM D1238 | 23 |
g/10 min
|
醋酸乙烯含量 | ExxonMobil Method | 18.5 |
wt%
|
||
机械性能 | 割线模量 |
1% 正割, MD
|
ASTM D882 | 50.9 |
MPa
|
1% 正割, TD
|
ASTM D882 | 55.3 |
MPa
|
||
抗张强度 |
MD: 断裂
|
ASTM D882 | 21.6 |
MPa
|
|
TD: 断裂
|
ASTM D882 | 14.9 |
MPa
|
||
伸长率 |
MD: 断裂
|
ASTM D882 | 530 |
%
|
|
TD: 断裂 | ASTM D882 | 810 |
%
|
||
落锤冲击 |
|
ASTM D1709A | 94 |
g
|
|
埃尔曼多夫抗撕强度 | MD | ASTM D1922 | 240 |
g
|
|
TD
|
ASTM D1922 | 330 |
g
|
||
热性能 | 维卡软化温度 | ASTM D1525 | 54.0 |
°C
|