密度 | 0.938g/cm3 | 熔体流动速率 | 19g/10min | 维卡软化点 | 60℃ |
硬度 | 34 | 规格级别 | 注塑 | 脆化温度 | -76℃ |
加工级别 | 注塑级,热熔级 |
|
产品简述
密度 | 0.938g/cm3 | 熔体流动速率 | 19g/10min | 维卡软化点 | 60℃ |
硬度 | 34 | 规格级别 | 注塑 | 脆化温度 | -76℃ |
加工级别 | 注塑级,热熔级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.938 | g/cm3 | ||
其它性能 | 铸膜成型 | ASTM D-638/D-882 | 790 | % | ||
融化点 | ASTM D-2117 | 82 | ℃ | |||
熔融指数 | ASTM D-1238 | 19 | g/10min | |||
薄膜 | MD | ASTM D-638/D-882 | 138 | kg/cm2 | ||
TD | ASTM D-638/D-882 | 86 | kg/cm2 | |||
射出 | ASTM D-638/D-882 | 300 | % | |||
VA含量 | ASTM USIFE | 20 | % | |||
薄膜 | MD | ASTM D-638/D-882 | 450 | % | ||
TD | ASTM D-638/D-882 | 660 | % | |||
硬度 | ASTM D-2240 | 34 | Shore D | |||
铸膜成型 | ASTM D-638 | 127 | kg/cm2 | |||
低温易脆性 | ASTM D-746 | <-76 | ℃/F50 | |||
VICAT 软化点 | ASTM D-1525 | 60 | ℃ | |||
射出 | ASTM D-638/D-882 | 72 | kg/cm2 |