断裂伸长率 | 400% | 拉伸强度 | 67MPa | 密度 | 0.32g/cm3 |
熔体流动速率 | 0.951g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
|
产品简述
断裂伸长率 | 400% | 拉伸强度 | 67MPa | 密度 | 0.32g/cm3 |
熔体流动速率 | 0.951g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.08 | g/10min | |||
熔体流动速率 | 190℃/5kg | ASTM D-1238 | 0.32 | g/10min | ||||
熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 11.0 | g/10min | ||||
密度 | ASTM D-792 | 0.951 | g/cm3 | |||||
机械性能 | 落镖冲击 | ASTM D-1709A | 350 | g | ||||
埃尔曼多夫撕裂强度 | ASTM D-1922 |
|
g | |||||
屈服拉伸强度 | 20in/min | ASTM D-882 |
|
psi | ||||
断裂拉伸强度 | 20in/min | ASTM D-882 |
|
psi | ||||
断裂伸长率 | 20in/min | ASTM D-882 |
|
% | ||||
2%正割模量 | 20in/min | ASTM D-882 |
|
psi | ||||
WVTR | E 96/66 | 0.8 | ||||||
热性能 | 熔点 | ASTM D-3417 | 270 | ℉ |