| 断裂伸长率 | 410% | 拉伸强度 | 68.8MPa | 密度 | 0.95g/cm3 |
| 熔体流动速率 | 9g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
| 缺口冲击强度 | 350 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
用途:挤压，吹薄用
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-792 | 0.950 | g/cm3 | ||
| 熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 9.0 | g/10min | ||
| 薄膜厚度 | 0.500 | mil | ||||
| 熔点 | DSC | 128 | ℃ | |||
| 机械性能 | 切割模量 | MD | ASTM D-882 | 965.2 | MPa | |
| TD | ASTM D-882 | 1096.2 | MPa | |||
| 屈服拉伸强度 | MD | ASTM D-882 | 42.3 | MPa | ||
| TD | ASTM D-882 | 31.7 | MPa | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 93.7 | MPa | ||
| TD | ASTM D-882 | 68.8 | MPa | |||
| 断裂伸长率 | MD | ASTM D-882 | 330 | % | ||
| TD | ASTM D-882 | 410 | % | |||
| 缺口冲击强度 | ASTM D-1709 | 350 | g | |||
| 埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 11 | g | ||
| TD | ASTM D-1922 | 73 | g | |||
| 光学性能 | 光泽度 | ASTM D-2457 | 9 | |||
| 雾度 | ASTM D-1003 | 69 | % | |||