断裂伸长率 | 610% | 拉伸强度 | 49MPa | 密度 | 0.952g/cm3 |
熔体流动速率 | 0.15g/10min | 维卡软化点 | 125℃ | 用途级别 | 薄膜级 |
规格级别 | 薄膜 |
|
产品简述
断裂伸长率 | 610% | 拉伸强度 | 49MPa | 密度 | 0.952g/cm3 |
熔体流动速率 | 0.15g/10min | 维卡软化点 | 125℃ | 用途级别 | 薄膜级 |
规格级别 | 薄膜 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.952 | g/cm3 | ||
熔体流动速率 | ASTM D-1238 | 0.15 | g/10min | |||
HLMI | ASTM D-1238 | 16 | g/10min | |||
机械性能 | 1%割线模量 | MD | ASTM D-882 | 1400 | MPa | |
TD | ASTM D-882 | 1700 | MPa | |||
断裂拉伸强度 | MD | ASTM D-882 | 55 | MPa | ||
TD | ASTM D-882 | 49 | MPa | |||
断裂伸长率 | MD | ASTM D-882 | 400 | MPa | ||
TD | ASTM D-882 | 610 | MPa | |||
屈服拉伸强度 | MD | ASTM D-1505 | 31 | MPa | ||
TD | ASTM D-1505 | 30 | MPa | |||
Elmendorf断裂强度 | MD | ASTM D-1922 | 4 | g | ||
TD | ASTM D-1922 | 40 | g | |||
Dart冲击强度 | F50 | ASTM D-1709 | 180 | g | ||
热性能 | 维卡软化点 | ASTM D-1525 | 125 | ℃ |