断裂伸长率 | 500% | 拉伸强度 | 29MPa | 密度 | 0.956g/cm3 |
熔体流动速率 | 0.044g/10min | 规格级别 | 薄膜级 | 缺口冲击强度 | 30 |
|
产品简述
断裂伸长率 | 500% | 拉伸强度 | 29MPa | 密度 | 0.956g/cm3 |
熔体流动速率 | 0.044g/10min | 规格级别 | 薄膜级 | 缺口冲击强度 | 30 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
密度 | ASTM D-1505 | 0.956 | g/cm3 | |
Dart Drop冲击强度 | ASTM D-1709 | >200 | g | |
Lzod缺口冲击强度 | ASTM D-256 | >30 | kg.cm/cm | |
撕裂强度(MD) | ASTM D-882 | 6 | kg/cm2 | |
撕裂强度(TD) | ASTM D-882 | 200 | kg/cm2 | |
断裂拉伸强度 | ASTM D-638 | 300 | kg/cm2 | |
屈服拉伸强度 | ASTM D-638 | 230 | kg/cm2 | |
Dart Drop冲击强度 | ASTM D-1709 | >200 | g | |
断裂拉伸强度(MD) | ASTM D-882 | 550 | kg/cm2 | |
断裂拉伸强度(TD) | ASTM D-882 | 500 | kg/cm2 | |
维卡软化点 | ASTM D-1525 | 124 | ℃ | |
弯曲模量 | ASTM D-747 | 10000 | kg/cm2 | |
熔点 | ASTM SGC | 131 | ℃ | |
洛氏硬度 | ASTM D-785 | 55 | R scale | |
熔融指数 | 190℃,2.16kg | ASTM D-1238 | 0.044 | g/10min |
ESCR | ASTM D-1693 | >1000 | Hrs | |
断裂伸长率 | ASTM D-638 | 500 | % | |
伸长率(MD) | ASTM D-882 | 380 | % | |
伸长率(TD) | ASTM D-882 | 450 | % | |
脆化温度 | ASTM D-746 | ℃ |