断裂伸长率 | 950% | 拉伸强度 | 29.5MPa | 密度 | 0.946g/cm3 |
熔体流动速率 | 0.3g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
|
产品简述
断裂伸长率 | 950% | 拉伸强度 | 29.5MPa | 密度 | 0.946g/cm3 |
熔体流动速率 | 0.3g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.946 | g/cc | ||
熔体流动速率 | 2.16kg | ASTM D-1238 | 0.30 | g/10min | ||
机械性能 | Dart冲击强度 | F50,38mm Dart,66cm height | ASTM D-1709 | 2.0 | g/μm | |
断裂伸长率 | MD | ASTM D-882 | 750 | % | ||
TD | ASTM D-882 | 950 | % | |||
撕裂强度 | MD | ASTM D-1922 | 0.8 | g/μm | ||
TD | ASTM D-1922 | 13.0 | g/μm | |||
屈服拉伸强度 | MD | ASTM D-882 | 26.5 | MPa | ||
TD | ASTM D-882 | 29.5 | MPa | |||
最终拉伸强度 | MD | ASTM D-882 | 55 | MPa | ||
TD | ASTM D-882 | 50 | MPa |