断裂伸长率 | 900% | 拉伸强度 | 50MPa | 密度 | 0.3g/cm3 |
用途级别 | 薄膜级 | 规格级别 | 薄膜 | 加工级别 | 注塑级 |
特性级别 | 增强级 |
|
产品简述
断裂伸长率 | 900% | 拉伸强度 | 50MPa | 密度 | 0.3g/cm3 |
用途级别 | 薄膜级 | 规格级别 | 薄膜 | 加工级别 | 注塑级 |
特性级别 | 增强级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 0.30 | g/10min | ||
密度 | ASTM D-1505 | 0.956 | g/cc | |||
机械性能 | Dart 冲击强度 | 38 mm Dart,66 cm height | ASTM D-1709 | 1.6 | g/µm | |
断裂拉伸强度 | MD | ASTM D-882 | 55.0 | MPa | ||
TD | ASTM D-882 | 50.0 | MPa | |||
拉伸屈服强度 | MD | ASTM D-882 | 35 | MPa | ||
TD | ASTM D-882 | 37 | MPa | |||
撕裂强度 | MD | ASTM D-1922 | 0.7 | g/µm | ||
TD | ASTM D-1922 | 10 | g/µm | |||
断裂伸长率 | MD | ASTM D-882 | 700 | % | ||
TD | ASTM D-882 | 900 | % |