断裂伸长率 | 5% | 拉伸强度 | 37.2MPa | 密度 | 0.958g/cm3 |
熔体流动速率 | 0.45g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 46 |
|
产品简述
断裂伸长率 | 5% | 拉伸强度 | 37.2MPa | 密度 | 0.958g/cm3 |
熔体流动速率 | 0.45g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 46 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 0.45 | g/10min | ||
熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 30 | g/10min | ||
密度 | 埃克森美孚法 | 0.958 | g/cm3 | |||
机械性能 | 屈服拉伸强度 | MD | ASTM D-882 | 34.3 | MPa | |
TD | ASTM D-882 | 19 | MPa | |||
断裂拉伸强度 | MD | ASTM D-882 | 73.8 | MPa | ||
TD | ASTM D-882 | 37.2 | MPa | |||
断裂伸长率 | MD | ASTM D-882 | 430 | % | ||
TD | ASTM D-882 | 5 | % | |||
切割模量 | MD | 1% | ASTM D-882 | 1150 | MPa | |
TD | 1% | ASTM D-882 | 1731 | MPa | ||
落镖冲击强度 | ASTM D-1709A | <46 | g | |||
埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 9 | g | ||
TD | ASTM D-1922 | 800 | g |