拉伸强度 | 38MPa | 密度 | 1.04g/cm3 | 熔体流动速率 | 3g/10min |
缺口冲击强度 | 75 | 成型收缩率 | 0.6% | 特性级别 | 阻燃级,抗静电 |
|
产品简述
拉伸强度 | 38MPa | 密度 | 1.04g/cm3 | 熔体流动速率 | 3g/10min |
缺口冲击强度 | 75 | 成型收缩率 | 0.6% | 特性级别 | 阻燃级,抗静电 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 熔体流动速率 | 200℃/5Kg | ASTM D-1238 | 3 | g/10min |
成型收缩率 | ASTM D-955 | 0.4~0.8 | % | ||
比重 | ASTM D-792 | 1.04 | |||
机械性能 | 延伸率 | ASTM D-638 | 40 | % | |
抗张强度 | ASTM D-638 | 380 | kg/cm2 | ||
弯曲弹性率 | ASTM D-790 | 650 | kg/cm2 | ||
冲击强度 | Notched 1/4" | ASTM D-256 | 5 | Kg/cm/cm | |
冲击强度 | Notched1/8" | ASTM D-256 | 75 | Kg/cm/cm | |
洛氏硬度 | R-Scale | ASTM D-785 | 110 | ||
挠曲模量 | ASTM D-790 | 27.000 | kg/cm2 | ||
电气性能 | HWI | UL 746A | 3 | PLC | |
抗弧光 | ASTM D-495 | 5 | PLC | ||
HAI | UL 746A | 0 | PLC | ||
CTI | UL 746A | 1 | PLC | ||
HVTR | UL 746A | 3 | PLC | ||
热性能 | 维卡软化点 | 1.000g | ASTM D-1525 | 101 | ℃ |
燃烧率 | 1/16" | UL 94 | HB | ||
热变形温度 | Unannealed18.5g/cm2,1/4" | ASTM D-648 | 80 | ℃ | |
燃烧率 | 1/8" | UL 94 | HB | ||
燃烧率 | 1/8" | IEC 707 | FH3-30 | mm/min |