断裂伸长率 | 620% | 拉伸强度 | 21.5MPa | 密度 | 0.924g/cm3 |
熔体流动速率 | 0.7g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 130 |
|
产品简述
断裂伸长率 | 620% | 拉伸强度 | 21.5MPa | 密度 | 0.924g/cm3 |
熔体流动速率 | 0.7g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 130 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-792 | 0.924 | g/cm3 | ||
熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.70 | g/10min | ||
机械性能 | 屈服拉伸强度 | MD | ASTM D-882 | 10.5 | MPa | |
TD | ASTM D-882 | 11.0 | MPa | |||
断裂拉伸强度 | MD | ASTM D-882 | 25.4 | MPa | ||
TD | ASTM D-882 | 21.5 | MPa | |||
断裂伸长率 | MD | ASTM D-882 | 330 | % | ||
TD | ASTM D-882 | 620 | % | |||
冲击强度 | ASTM D-1709 | 130 | g | |||
埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 270 | g | ||
TD | ASTM D-1922 | 190 | g | |||
其它性能 | 薄膜厚度 | 38.1 | μ | |||
薄膜硬度 | MD | ASTM D-882 | 66.4 | J/CM3 | ||
TD | ASTM D-882 | 79.0 | J/CM3 | |||
光学性能 | 光泽度 | 45° | ASTM D-2457 | 55 | ||
雾度 | ASTM D-1003 | 9.9 | % |