断裂伸长率 | 700% | 拉伸强度 | 15MPa | 密度 | 0.925g/cm3 |
熔体流动速率 | 2.8g/10min | 规格级别 | 薄膜级 | 缺口冲击强度 | 65 |
|
产品简述
断裂伸长率 | 700% | 拉伸强度 | 15MPa | 密度 | 0.925g/cm3 |
熔体流动速率 | 2.8g/10min | 规格级别 | 薄膜级 | 缺口冲击强度 | 65 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
密度 | ASTM D-1505 | 0.925 | g/cm3 | |
熔体流动速率 | 190℃ | ASTM D-1238 | 2.8 | g/10min |
摩擦系数 | ASTM D-1894 | 0.05 | ||
薄雾 | ASTM D-1003 | 7 | % | |
断裂拉伸强度(MD) | ASTM D-882 | 230 | KG/cm2 | |
断裂拉伸强度(TD) | ASTM D-882 | 160 | KG/cm2 | |
屈服拉伸强度 | 50mm/min | ASTM D-638 | 130 | kg/cm2 |
弯曲模数 | ASTM D-747 | 2800 | kg/cm2 | |
断裂延伸率 | ASTM D-638 | 700 | % | |
Dart drop impact | ASTM D-1709 | 65 | G | |
断裂拉伸强度 | 50mm/min | ASTM D-638 | 130 | kg/cm2 |
伸长率(MD) | 240 | % | ||
伸长率(TD) | 590 | % | ||
熔点 | SGC | 112.5 | ||
维卡软化点 | 1KG | ASTM D-1525 | 95 | ℃ |
Brittleness Temperature | ASTM D-746 | <-70 | ||
Blocking | SGC | 240 | g/10cm2 |