断裂伸长率 | 570% | 拉伸强度 | 17.9MPa | 密度 | 0.924g/cm3 |
熔体流动速率 | 0.88g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 120 | 加工级别 | 注塑级 | 特性级别 | 增强级 |
|
产品简述
断裂伸长率 | 570% | 拉伸强度 | 17.9MPa | 密度 | 0.924g/cm3 |
熔体流动速率 | 0.88g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 120 | 加工级别 | 注塑级 | 特性级别 | 增强级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-792 | 0.924 | g/cm3 | ||
熔体流动速率 | ASTM D-1238 | 0.88 | g/10min | |||
薄膜厚度 | 50.8 | μ | ||||
机械性能 | 切割模量 | MD | ASTM D-882 | 202 | MPa | |
TD | ASTM D-882 | 228 | MPa | |||
屈服拉伸强度 | MD | ASTM D-882 | 11.7 | MPa | ||
TD | ASTM D-882 | 12.2 | MPa | |||
断裂拉伸强度 | MD | ASTM D-882 | 21.5 | MPa | ||
TD | ASTM D-882 | 17.9 | MPa | |||
断裂伸长率 | MD | ASTM D-882 | 370 | % | ||
TD | ASTM D-882 | 570 | % | |||
落镖冲击强度 | ASTM D-1709 | 120 | g | |||
埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 430 | g | ||
TD | ASTM D-1922 | 480 | g | |||
热性能 | 维卡软化点 | ASTM D-1525 | 97.2 | ℃ | ||
熔点 | DSC | 112 | ℃ | |||
光学性能 | 光泽度 | ASTM D-2457 | 76 | |||
雾度 | ASTM D-1003 | 7.0 | % |