| 断裂伸长率 | 600% | 拉伸强度 | 18MPa | 密度 | 0.924g/cm3 |
| 熔体流动速率 | 0.8g/10min | 弯曲模量 | 176MPa |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
用途:收缩膜、积压膜、中空吹制。
备注:特性：收缩性优、光学优良、刚性适中。
备注:特性：收缩性优、光学优良、刚性适中。
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.924 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 0.8 | g/10min | |||
| 机械性能 | 抗撕裂性 | MD | ASTM D-1922 | 45 | N/mm | |
| TD | ASTM D-1922 | 60 | N/mm | |||
| 拉力降伏强度 | MD | ASTM D-882B | 100 | kg/cm2 | ||
| TD | ASTM D-882B | 110 | kg/cm2 | |||
| 拉力降伏强度 | ASTM D-638 | 120 | kg/cm2 | |||
| 拉力断裂强度 | ASTM D-638 | 170 | kg/cm2 | |||
| 硬度 | ASTM D-2240 | 54 | Shore D | |||
| 摩擦系数 | ASTM D-1894 | >0.5 | ||||
| 落球行动强度 | ASTM D-1709 | 260 | g | |||
| 弯曲模量 | ASTM D-790 | 1800 | kg/cm2 | |||
| 拉力断裂伸长率 | ASTM D-638 | 700 | % | |||
| 拉力断裂伸长率 | MD | ASTM D-882B | 380 | % | ||
| TD | ASTM D-882B | 600 | % | |||
| 1%伸长弹性系数 | MD | ASTM D-882B | 1900 | kg/cm2 | ||
| TD | ASTM D-882B | 2150 | kg/cm2 | |||
| 拉力断裂强度 | MD | ASTM D-882B | 220 | kg/cm2 | ||
| TD | ASTM D-882B | 190 | kg/cm2 | |||
| 热性能 | 软化点 | ASTM D-1525 | 98 | ℃ | ||
| 熔点 | DSC | 113 | ℃ | |||
| 脆化温度 | ASTM D-746 | <-70 | ℃ | |||
| 其它性能 | 薄膜厚度 | ASTM D-1003 | 30～120 | µ | ||
| 浊度 | ASTM D-1003 | 10 | % | |||
| 光泽度45° | ASTM D-2457 | 70 | % | |||