断裂伸长率 | 650% | 拉伸强度 | 16MPa | 密度 | 0.92g/cm3 |
熔体流动速率 | 0.8g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 130 |
|
产品简述
断裂伸长率 | 650% | 拉伸强度 | 16MPa | 密度 | 0.92g/cm3 |
熔体流动速率 | 0.8g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 130 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.920 | g/cm3 | ||
熔体流动速率 | ASTM D-1238 | 0.80 | g/10min | |||
物理性能 | 光泽度 | 45℃ | ASTM D-2457 | 85 | ||
薄膜厚度 | HPC | 60 | μm | |||
雾度 | ASTM D-1003 | 7 | % | |||
机械性能 | 断裂拉伸强度 | MD | ASTM D-882 | 270 | kg/cm2 | |
TD | ASTM D-882 | 260 | kg/cm2 | |||
断裂伸长率 | MD | ASTM D-882 | 400 | % | ||
TD | ASTM D-882 | 600 | % | |||
伸长弹性率 | ASTM D-638 | 1150 | Kg/cm2 | |||
屈服拉伸强度 | ASTM D-638 | 88 | Kg/cm2 | |||
断裂伸长率 | ASTM D-638 | 650 | % | |||
肖氏硬度 | ASTM D-2240 | 50 | D SCALE | |||
断裂拉伸强度 | ASTM D-638 | 170 | Kg/cm2 | |||
落球冲击强度 | ASTM D-1709 | 130 | g | |||
热性能 | 维卡软化点 | ASTM D-1525 | 94 | |||
熔点 | HPC | 105 | ℃ |