断裂伸长率 | 650% | 拉伸强度 | 17MPa | 密度 | 0.92g/cm3 |
熔体流动速率 | 0.3g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 400 |
|
产品简述
断裂伸长率 | 650% | 拉伸强度 | 17MPa | 密度 | 0.92g/cm3 |
熔体流动速率 | 0.3g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 400 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | 23°C | ASTM D-1505 | 0.921 | g/cm3 | |
熔体流动速率 | ASTM D-1238 | 0.3 | g/10min | |||
机械性能 | 断裂伸长率 | ASTM D-638 | 650 | % | ||
破裂点张力 | MD | ASTM D-882 | 230 | kg/cm2 | ||
TD | ASTM D-882 | 220 | kg/cm2 | |||
断裂点伸张率 | MD | ASTM D-882 | 500 | % | ||
TD | ASTM D-882 | 550 | % | |||
屈服点张力 | ASTM D-638 | 100 | Kg/cm2 | |||
抗张强度 | ASTM D-638 | 180 | Kg/cm2 | |||
跌落冲击强度 | ASTM D-1709 | 400 | g | |||
抗撕裂张度 | MD | ASTM D-1922 | 370 | g | ||
TD | ASTM D-1922 | 780 | g | |||
热性能 | 维卡软化点 | ASTM D-1525 | 95 | °C | ||
低温脆化温度 | ASTM D-746 | <-76 | °C |