断裂伸长率 | 500% | 拉伸强度 | 17MPa | 密度 | 0.923g/cm3 |
熔体流动速率 | 1.2g/10min | 用途级别 | 薄膜级,食品级 | 规格级别 | 薄膜 |
缺口冲击强度 | 150 |
|
产品简述
断裂伸长率 | 500% | 拉伸强度 | 17MPa | 密度 | 0.923g/cm3 |
熔体流动速率 | 1.2g/10min | 用途级别 | 薄膜级,食品级 | 规格级别 | 薄膜 |
缺口冲击强度 | 150 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 1.2 | g/10min | ||
密度 | 23℃ | ASTM D-1505 | 0.923 | g/cm3 | ||
机械性能 | 拉伸屈服强度 | MD | ASTM D-882 | 19 | MPa | |
TD | ASTM D-882 | 12 | MPa | |||
抗冲击强度 | ASTM D-1709 | 150 | g | |||
断裂伸长率 | MD | ASTM D-882 | 370 | % | ||
TD | ASTM D-882 | 500 | % | |||
断裂拉伸强度 | MD | ASTM D-882 | 22 | MPa | ||
TD | ASTM D-882 | 17 | MPa | |||
热性能 | 维卡软化点 | ASTM D-1525 | 95 | ℃ | ||
晶体熔点 | ASTM E-794 | 112 | ℃ | |||
其它性能 | 雾度(浊度) | ASTM D-1003 | 8.5 | % | ||
光泽度 | ASTM D-2457 | 70 | gu | |||
推荐薄膜厚度 | 30-200 | µm | ||||
摩擦系数 | ASTM D-1894 | 0.20 | ||||
透明度 | ASTM D-1746 | 50 | % |