断裂伸长率 | 560% | 拉伸强度 | 23MPa | 密度 | 0.922g/cm3 |
熔体流动速率 | 0.75g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 4 |
|
产品简述
断裂伸长率 | 560% | 拉伸强度 | 23MPa | 密度 | 0.922g/cm3 |
熔体流动速率 | 0.75g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 4 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 0.75 | g/10min | ||
密度 | ASTM D-1505 | 0.922 | g/cm3 | |||
物理性能 | 光泽 | 60度 | ASTM D-2457 | 9 | ||
机械性能 | Elmendorf断裂强度 | MD | ASTM D-1922 | 4 | ||
TD | ASTM D-1922 | 7 | ||||
断裂伸长率 | MD | ASTM D-882 | 370 | % | ||
TD | ASTM D-882 | 560 | % | |||
屈服点 | ASTM D-882|ASTM D-882 | 12|12 | MPa|MPa | |||
断裂拉伸 | MD | ASTM D-882 | 26 | MPa | ||
TD | ASTM D-882 | 23 | MPa | |||
Dart冲击强度 | ASTM D-1709 | 4 | ||||
1%割线模量 | MD | ASTM D-882 | 220 | MPa | ||
TD | ASTM D-882 | 240 | MPa | |||
热性能 | 维卡软化点 | ASTM D-1525 | 98 | ℃ | ||
其它性能 | 混浊 | ASTM D-1003 | 6.5 | % |