断裂伸长率 | 520% | 拉伸强度 | 19MPa | 密度 | 0.922g/cm3 |
熔体流动速率 | 2g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 3 | 特性级别 | 透明级 |
|
产品简述
断裂伸长率 | 520% | 拉伸强度 | 19MPa | 密度 | 0.922g/cm3 |
熔体流动速率 | 2g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 3 | 特性级别 | 透明级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 2.0 | g/10min | ||
维卡软化点 | ASTM D-1525 | 94 | ℃ | |||
密度 | ASTM D-1505 | 0.922 | g/cm3 | |||
物理性能 | 混浊 | ASTM D-1003 | 6 | % | ||
光泽度 | 60℃ | ASTM D-2457 | 10.5 | |||
机械性能 | 1%割线模量 | MD | ASTM D-882 | 210 | MPa | |
TD | ASTM D-882 | 250 | MPa | |||
Dart冲击强度 | ASTM D-1709 | 3 | ||||
屈服点 | MD | ASTM D-882 | 12 | MPa | ||
TD | ASTM D-882 | 11 | MPa | |||
断裂伸长率 | MD | ASTM D-882 | 240 | % | ||
TD | ASTM D-882 | 520 | % | |||
断裂拉伸 | MD | ASTM D-882 | 22 | MPa | ||
TD | ASTM D-882 | 19 | MPa | |||
Elmendorf断裂强度 | MD | ASTM D-1938 | 8 | |||
TD | ASTM D-1938 | 4.5 |