断裂伸长率 | 480% | 拉伸强度 | 21MPa | 密度 | 0.922g/cm3 |
熔体流动速率 | 0.55g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 700 |
|
产品简述
断裂伸长率 | 480% | 拉伸强度 | 21MPa | 密度 | 0.922g/cm3 |
熔体流动速率 | 0.55g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 700 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.922 | g/cm3 | ||
熔体流动速率 | ASTM D-1238 | 0.55 | g/10min | |||
物理性能 | 试根厚度 | DICM | 200 | μM | ||
模糊度 | ASTM D-1709 | 10 | % | |||
机械性能 | ELMENDORF拉力强度 | MD | ASTM D-1922 | 450 | g | |
TD | ASTM D-1922 | 550 | g | |||
破断点伸度 | MD | ASTM D-882 | 440 | % | ||
TD | ASTM D-882 | 480 | % | |||
破断点抗张强度 | MD | ASTM D-882 | 240 | Kg/cm2 | ||
TD | ASTM D-882 | 220 | Kg/cm2 | |||
拉力强度 | MD | ASTM D-1922 | 105 | g | ||
TD | ASTM D-1922 | 100 | g | |||
落球冲击强度 | ASTM D-882 | 700 | Kg/cm2 |