断裂伸长率 | 470% | 拉伸强度 | 21MPa | 密度 | 0.921g/cm3 |
熔体流动速率 | 0.5g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 650 |
|
产品简述
断裂伸长率 | 470% | 拉伸强度 | 21MPa | 密度 | 0.921g/cm3 |
熔体流动速率 | 0.5g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 650 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.921 | g/cm3 | ||
熔体流动速率 | ASTM D-1238 | 0.5 | g/10min | |||
物理性能 | 模糊度 | ASTM D-1709 | 17 | % | ||
试根厚度 | DICM | 200 | μM | |||
机械性能 | 破断点伸度 | MD | ASTM D-882 | 440 | % | |
TD | ASTM D-882 | 470 | % | |||
ELMENDORF拉力强度 | MD | ASTM D-1922 | 740 | g | ||
TD | ASTM D-1922 | 752 | g | |||
拉力强度 | MD | ASTM D-1922 | 100 | g | ||
TD | ASTM D-1922 | 100 | g | |||
落球冲击强度 | ASTM D-882 | 650 | Kg/cm2 | |||
破断点抗张强度 | MD | ASTM D-882 | 230 | Kg/cm2 | ||
TD | ASTM D-882 | 220 | Kg/cm2 |