断裂伸长率 | 580% | 拉伸强度 | 19MPa | 密度 | 0.921g/cm3 |
熔体流动速率 | 3g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 90 |
|
产品简述
断裂伸长率 | 580% | 拉伸强度 | 19MPa | 密度 | 0.921g/cm3 |
熔体流动速率 | 3g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 90 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 3.0 | g/10min | ||
密度 | ASTM D-1505 | 0.921 | g/cm3 | |||
物理性能 | 模糊度 | ASTM D-1709 | 6 | % | ||
试根厚度 | DICM | 30 | μM | |||
机械性能 | 拉力强度 | MD | ASTM D-1922 | 95 | g | |
TD | ASTM D-1922 | 90 | g | |||
落球冲击强度 | ASTM D-882 | 90 | Kg/cm2 | |||
ELMENDORF拉力强 | MD | ASTM D-1922 | 300 | g | ||
TD | ASTM D-1922 | 210 | g | |||
破断点伸度 | MD | ASTM D-882 | 450 | % | ||
TD | ASTM D-882 | 580 | % | |||
破断点抗张强度 | MD | ASTM D-882 | 210 | Kg/cm2 | ||
TD | ASTM D-882 | 195 | Kg/cm2 |