断裂伸长率 | 741% | 拉伸强度 | 23MPa | 密度 | 0.919g/cm3 |
熔体流动速率 | 2g/10min | 维卡软化点 | 96℃ | 用途级别 | 薄膜级 |
规格级别 | 薄膜 | 加工级别 | 注塑级 | 特性级别 | 增强级 |
|
产品简述
断裂伸长率 | 741% | 拉伸强度 | 23MPa | 密度 | 0.919g/cm3 |
熔体流动速率 | 2g/10min | 维卡软化点 | 96℃ | 用途级别 | 薄膜级 |
规格级别 | 薄膜 | 加工级别 | 注塑级 | 特性级别 | 增强级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 2 | g/10min | ||
密度 | ASTM D-792 | 0.919 | g/cc | |||
机械性能 | Dart 冲击强度 | ASTM D-1709 | <175 | g | ||
拉伸模量 | MD | ASTM D-882 | 167.4 | MPa | ||
TD | ASTM D-882 | 207 | MPa | |||
断裂伸长率 | MD | ASTM D-882 | 715 | % | ||
TD | ASTM D-882 | 741 | % | |||
刺穿强度 | DOW | 6.5 | J/cm3 | |||
屈服拉伸强度 | MD | ASTM D-882 | 10.2 | MPa | ||
TD | ASTM D-882 | 10.6 | MPa | |||
抗撕裂性 | MD | ASTM D-1922 | 107 | g | ||
TD | ASTM D-1922 | 218 | g | |||
断裂拉伸强度 | MD | ASTM D-882 | 27.4 | MPa | ||
TD | ASTM D-882 | 23.0 | MPa | |||
热性能 | 维卡软化点 | ASTM D-1525 | 96 | ℃ | ||
熔点 | DOW | 104 | ℃ | |||
其它性能 | 韧性 | MD | ASTM D-882 | 102.5 | J/cm3 | |
TD | ASTM D-882 | 96.7 | J/cm3 | |||
雾度 | ASTM D-1003 | 13.5 | % | |||
光泽度 | 20℃ | ASTM D-2457 | 60 | |||
透明度 | ASTM D-1746 | 94 |