| 断裂伸长率 | 710% | 拉伸强度 | 24MPa | 密度 | 0.918g/cm3 |
| 熔体流动速率 | 2g/10min | 维卡软化点 | 93℃ | 用途级别 | 薄膜级 |
| 规格级别 | 薄膜 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
用途:用途：机械捆包膜。
备注:特性：高刺穿强度，薄膜延伸性佳，押出性佳，高强度。
备注:特性：高刺穿强度，薄膜延伸性佳，押出性佳，高强度。
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.918 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 2.0 | g/10min | |||
| 机械性能 | 落球冲击强度 | ASTM D-1709 | 150 | g | ||
| 抗撕裂性 | MD | ASTM D-1922 | 260 | g/25µm | ||
| TD | ASTM D-1922 | 570 | g/25µm | |||
| 拉力降伏强度 | MD | ASTM D-882B | 100 | kg/cm2 | ||
| TD | ASTM D-882B | 110 | kg/cm2 | |||
| 1%伸长弹性系数 | MD | ASTM D-882B | 1800 | kg/cm2 | ||
| TD | ASTM D-882B | 1700 | kg/cm2 | |||
| 拉力断裂伸长率 | MD | ASTM D-882B | 540 | % | ||
| TD | ASTM D-882B | 710 | % | |||
| 拉力断裂强度 | MD | ASTM D-882B | 330 | kg/cm2 | ||
| TD | ASTM D-882B | 250 | kg/cm2 | |||
| 热性能 | 脆化温度 | ASTM D-746 | <-70 | ℃ | ||
| 熔点 | FPC | 121 | ℃ | |||
| 软化点 | ASTM D-1525 | 93 | ℃ | |||
| 其它性能 | 透明度 | 95 | % | |||
| 抗粘剂 | 无 | |||||
| 滑剂 | 无 | |||||
| 光泽度 | 45℃ | ASTM D-2457 | 96 | % | ||
| 浊度 | ASTM D-1003 | 3 | % | |||