断裂伸长率 | 610% | 拉伸强度 | 18MPa | 密度 | 0.918g/cm3 |
熔体流动速率 | 2.8g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
|
产品简述
断裂伸长率 | 610% | 拉伸强度 | 18MPa | 密度 | 0.918g/cm3 |
熔体流动速率 | 2.8g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-792 | 0.918 | g/cm3 | ||
熔体流动速率 | ASTM D-1238 | 2.8 | g/10min | |||
物理性能 | 混浊 | ASTM D-1003 | 1.5 | % | ||
光泽度 | 60℃ | ASTM D-2457 | 90 | |||
机械性能 | 断裂拉伸强度 | MD | ASTM D-882 | 30 | MPa | |
TD | ASTM D-882 | 18.5 | MPa | |||
断裂伸长率 | MD | ASTM D-882 | 470 | % | ||
TD | ASTM D-882 | 610 | % | |||
屈服拉伸强度 | MD | ASTM D-882 | 13 | MPa | ||
TD | ASTM D-882 | 10 | MPa | |||
抗穿刺强度 | SABIC | 57 | J/mm | |||
落锤冲击 | F50 | ASTM D-1709 | 76 | G | ||
1%割线模量 | MD | ASTM D-882 | 136 | MPa | ||
TD | ASTM D-882 | 142 | MPa | |||
门氏撕裂强度 | MD | ASTM D-1922 | 65 | g | ||
TD | ASTM D-1922 | 300 | g |