| 断裂伸长率 | 800% | 拉伸强度 | 27MPa | 密度 | 0.92g/cm3 |
| 熔体流动速率 | 2g/10min | 维卡软化点 | 93℃ | 用途级别 | 薄膜级 |
| 规格级别 | 玻璃珠增强 | 特性级别 | 耐磨,增强级,阻燃级,耐高温 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
用途:各类购物袋，轻、中包装膜，超薄膜，伸缩膜。
备注:特性：热封性佳，薄膜延伸性佳，押出性佳。
备注:特性：热封性佳，薄膜延伸性佳，押出性佳。
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.920 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 2.0 | g/10min | |||
| 机械性能 | 落球冲击强度 | ASTM D-1709 | 120 | g | ||
| 1%伸长弹性系数 | MD | ASTM D-882B | 1500 | kg/cm2 | ||
| TD | ASTM D-882B | 2100 | kg/cm2 | |||
| 抗撕裂性 | MD | ASTM D-1922 | 40 | g/25µm | ||
| TD | ASTM D-1922 | 430 | g/25µm | |||
| 拉力断裂伸长率 | MD | ASTM D-882B | 600 | % | ||
| TD | ASTM D-882B | 800 | % | |||
| 拉力降伏强度 | MD | ASTM D-882B | 100 | kg/cm2 | ||
| TD | ASTM D-882B | 110 | kg/cm2 | |||
| 拉力断裂强度 | MD | ASTM D-882B | 360 | kg/cm2 | ||
| TD | ASTM D-882B | 280 | kg/cm2 | |||
| 热性能 | 脆化温度 | ASTM D-746 | <-70 | ℃ | ||
| 熔点 | DSC | 122 | ℃ | |||
| 软化点 | ASTM D-1525 | 93 | ℃ | |||
| 其它性能 | 滑剂 | 无 | ||||
| 光泽度 | 45℃ | ASTM D-2457 | 43 | % | ||
| 开口剂 | 无 | |||||
| 浊度 | ASTM D-1003 | 21 | % | |||
| 透明度 | 67 | % | ||||