断裂伸长率 | 800% | 拉伸强度 | 27MPa | 密度 | 0.92g/cm3 |
熔体流动速率 | 2g/10min | 维卡软化点 | 93℃ | 加工级别 | 注塑级 |
|
产品简述
断裂伸长率 | 800% | 拉伸强度 | 27MPa | 密度 | 0.92g/cm3 |
熔体流动速率 | 2g/10min | 维卡软化点 | 93℃ | 加工级别 | 注塑级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 2.0 | g/10min | ||
密度 | ASTM D-1505 | 0.920 | g/cm3 | |||
机械性能 | 拉力断裂强度 | MD | ASTM D-882B | 360 | kg/cm2 | |
TD | ASTM D-882B | 280 | kg/cm2 | |||
落球冲击强度 | ASTM D-1709 | 120 | g | |||
拉力断裂伸长率 | MD | ASTM D-882B | 600 | % | ||
TD | ASTM D-882B | 800 | % | |||
拉力降伏强度 | MD | ASTM D-882B | 100 | kg/cm2 | ||
TD | ASTM D-882B | 110 | kg/cm2 | |||
1%伸长弹性系数 | MD | ASTM D-882B | 1500 | kg/cm2 | ||
TD | ASTM D-882B | 2100 | kg/cm2 | |||
抗撕裂性 | MD | ASTM D-1922 | 40 | g/25µm | ||
TD | ASTM D-1922 | 430 | g/25µm | |||
热性能 | 熔点 | DSC | 122 | ℃ | ||
软化点 | ASTM D-1525 | 93 | ℃ | |||
脆化温度 | ASTM D-746 | <-70 | ℃ | |||
其它性能 | 光泽度 | 45℃ | ASTM D-2457 | 50 | % | |
开口剂 | 高 | |||||
滑剂 | 中 | |||||
浊度 | ASTM D-1003 | 29 | % | |||
透明度 | 28 | % |