断裂伸长率 | 730% | 拉伸强度 | 40MPa | 密度 | 0.921g/cm3 |
熔体流动速率 | 0.8g/10min | 用途级别 | 薄膜级,纤维 | 规格级别 | 薄膜 |
特性级别 | 热稳定性,增强级,阻燃级 |
|
产品简述
断裂伸长率 | 730% | 拉伸强度 | 40MPa | 密度 | 0.921g/cm3 |
熔体流动速率 | 0.8g/10min | 用途级别 | 薄膜级,纤维 | 规格级别 | 薄膜 |
特性级别 | 热稳定性,增强级,阻燃级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | ASTM D-1238 | 0.8 | g/10min | ||
密度 | ASTM D-792 | 0.921 | g/cm3 | |||
物理性能 | 混浊 | ASTM D-1003 | 10.5 | % | ||
光泽度 | 60℃ | ASTM D-2457 | 70 | |||
机械性能 | 断裂伸长率 | MD | ASTM D-882 | 600 | % | |
TD | ASTM D-882 | 730 | % | |||
落锤冲击 | F50 | ASTM D-1709 | 160 | g | ||
断裂拉伸强度 | MD | ASTM D-882 | 55 | MPa | ||
TD | ASTM D-882 | 40 | MPa | |||
1%割线模量 | MD | ASTM D-882 | 210 | MPa | ||
TD | ASTM D-882 | 230 | MPa | |||
门氏撕裂强度 | MD | ASTM D-1922 | 300 | g | ||
TD | ASTM D-1922 | 915 | g | |||
屈服拉伸强度 | MD | ASTM D-882 | 12 | MPa | ||
TD | ASTM D-882 | 13 | MPa | |||
抗穿刺强度 | SABIC | 70 | J/mm |