断裂伸长率 | 850% | 拉伸强度 | 35MPa | 密度 | 0.919g/cm3 |
熔体流动速率 | 1g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 10 |
|
产品简述
断裂伸长率 | 850% | 拉伸强度 | 35MPa | 密度 | 0.919g/cm3 |
熔体流动速率 | 1g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
缺口冲击强度 | 10 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
其它性能 | 拉伸断裂强度 | MD | ASTM D-882 | 430 | Kg/cm2 | |
TD | ASTM D-882 | 360 | Kg/cm2 | |||
基本性能 | 密度 | ASTM D-1505 | 0.919 | g/cm3 | ||
熔体流动速率 | ASTM D-1238 | 1 | g/10min | |||
机械性能 | 拉伸屈服强度 | MD | ASTM D-882 | 120 | Kg/cm2 | |
TD | ASTM D-882 | 110 | Kg/cm2 | |||
伸长率 | MD | ASTM D-882 | 750 | % | ||
TD | ASTM D-882 | 850 | % | |||
撕裂强度 | MD | ASTM D-1004 | 5 | Kg/cm | ||
TD | ASTM D-1004 | 12 | Kg/cm | |||
抗冲击强度 | ASTM D-3420 | 10 | Kg/cm | |||
撕裂弹性率 | MD | ASTM D-882 | 2,000 | Kg/cm2 | ||
TD | ASTM D-882 | 2,500 | Kg/cm2 | |||
热性能 | 维卡软化点 | ASTM D-1525 | 102 | ℃ | ||
脆化温度 | ASTM D-746 | <-70 | ℃ | |||
其它性能 | 雾度 | ASTM D-1003 | 23 | % | ||
薄膜厚度 | ASTM D-746 | 50 | µm |