断裂伸长率 | 800% | 拉伸强度 | 34MPa | 密度 | 0.919g/cm3 |
熔体流动速率 | 1g/10min | 用途级别 | 薄膜级,薄壁制品 | 规格级别 | 薄膜 |
缺口冲击强度 | 10 |
|
产品简述
断裂伸长率 | 800% | 拉伸强度 | 34MPa | 密度 | 0.919g/cm3 |
熔体流动速率 | 1g/10min | 用途级别 | 薄膜级,薄壁制品 | 规格级别 | 薄膜 |
缺口冲击强度 | 10 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.919 | g/cm3 | ||
熔体流动速率 | ASTM D-1238 | 1 | g/10min | |||
物理性能 | 薄膜厚度 | ASTM D-746 | 25 | µm | ||
机械性能 | 撕裂强度 | MD | ASTM D-1004 | 125 | Kg/cm | |
TD | ASTM D-1004 | 105 | Kg/cm | |||
抗冲击强度 | ASTM D-3420 | 10 | Kg/cm | |||
撕裂弹性率 | MD | ASTM D-882 | 2000 | Kg/cm2 | ||
TD | ASTM D-882 | 2500 | Kg/cm2 | |||
断裂伸长率 | MD | ASTM D-882 | 650 | % | ||
TD | ASTM D-882 | 800 | % | |||
断裂拉伸强度 | MD | ASTM D-882 | 400 | Kg/cm2 | ||
TD | ASTM D-882 | 350 | Kg/cm2 | |||
屈服拉伸强度 | MD | ASTM D-882 | 120 | Kg/cm2 | ||
TD | ASTM D-882 | 110 | Kg/cm2 | |||
热性能 | 维卡软化点 | ASTM D-1525 | 102 | ℃ | ||
低温脆化温度 | ASTM D-746 | <-70 | % |