| 断裂伸长率 | 850% | 拉伸强度 | 68MPa | 密度 | 0.919g/cm3 |
| 熔体流动速率 | 0.9g/10min | 维卡软化点 | 102℃ | 用途级别 | 薄膜级,光学级 |
| 规格级别 | 薄膜 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
用途:拉伸覆盖材料，工业用薄膜。
备注:特性：抗张强度，热封合性
备注:特性：抗张强度，热封合性
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.919 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 0.9 | g/10min | |||
| 物理性能 | 薄膜厚度 | 25 | µm | |||
| 机械性能 | 尖头冲击强度 | ASTM D-1709 | 5 | g/μm | ||
| 拉伸断裂强度 | MD | ASTM D-882 | 400 | Kg/cm2 | ||
| TD | ASTM D-882 | 700 | Kg/cm2 | |||
| 撕裂强度 | MD | ASTM D-1004 | 130 | Kg/cm | ||
| TD | ASTM D-1004 | 120 | Kg/cm | |||
| 断裂伸长率 | MD | ASTM D-882 | 700 | % | ||
| TD | ASTM D-882 | 850 | % | |||
| 撕裂弹性率 | MD | ASTM D-882 | 2200 | Kg/cm2 | ||
| TD | ASTM D-882 | 3100 | Kg/cm2 | |||
| 拉伸屈服强度 | MD | ASTM D-882 | 140 | Kg/cm2 | ||
| TD | ASTM D-882 | 130 | Kg/cm2 | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 102 | ℃ | ||
| 低温脆化温度 | ASTM D-746 | <-80 | ℃ | |||