| 断裂伸长率 | 800% | 拉伸强度 | 32MPa | 密度 | 0.918g/cm3 |
| 熔体流动速率 | 2.1g/10min | 维卡软化点 | 98℃ | 用途级别 | 薄膜级,食品级 |
| 规格级别 | 薄膜 | 加工级别 | 吹膜级 | 特性级别 | 透明级 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
用途:T-模，工业用
备注:特性：抗张强度、加工性、透明性
备注:特性：抗张强度、加工性、透明性
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 2.1 | g/10min | ||
| 密度 | ASTM D-1505 | 0.918 | g/10min | |||
| 物理性能 | 薄膜厚度 | 25 | μm | |||
| 机械性能 | 断裂拉伸强度 | MD | ASTM D-882 | 380 | Kg/cm2 | |
| TD | ASTM D-882 | 330 | Kg/cm2 | |||
| 屈服拉伸强度 | MD | ASTM D-882 | 140 | Kg/cm2 | ||
| TD | ASTM D-882 | 130 | Kg/cm2 | |||
| 尖头冲击强度 | ASTM D-1709 | 3.5 | g/μm | |||
| 断裂伸长率 | MD | ASTM D-882 | 650 | % | ||
| TD | ASTM D-882 | 800 | % | |||
| 抗张模数 | MD | ASTM D-882 | 2200 | Kg/cm2 | ||
| TD | ASTM D-882 | 3100 | Kg/cm2 | |||
| 撕裂强度 | MD | ASTM D-1004 | 115 | kg/cm | ||
| TD | ASTM D-1004 | 105 | kg/cm | |||
| 热性能 | 低温脆化温度 | ASTM D-746 | <-75 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 98 | ℃ | |||