| 断裂伸长率 | 800% | 拉伸强度 | 40MPa | 密度 | 0.932g/cm3 |
| 熔体流动速率 | 2.7g/10min | 维卡软化点 | 110℃ | 用途级别 | 薄膜级 |
| 规格级别 | 薄膜 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
用途:T-模，尿布
备注:特性：抗张强度、加工性
备注:特性：抗张强度、加工性
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.932 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 2.7 | g/10min | |||
| 物理性能 | 薄膜厚度 | 25 | µm | |||
| 机械性能 | 撕裂强度 | MD | ASTM D-1004 | 130 | kg/cm | |
| TD | ASTM D-1004 | 120 | kg/cm | |||
| 断裂伸长率 | MD | ASTM D-638 | 650 | % | ||
| TD | ASTM D-638 | 800 | % | |||
| 拉伸屈服强度 | MD | ASTM D-638 | 180 | Kg/cm2 | ||
| TD | ASTM D-638 | 170 | Kg/cm2 | |||
| 拉伸断裂强度 | MD | ASTM D-638 | 440 | Kg/cm2 | ||
| TD | ASTM D-638 | 410 | Kg/cm2 | |||
| 尖头冲击强度 | ASTM D-1709 | 4.2 | g/μm | |||
| 抗张模数 | MD | ASTM D-882 | 3000 | Kg/cm2 | ||
| TD | ASTM D-882 | 4000 | Kg/cm2 | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 110 | ℃ | ||
| 低温脆化温度 | ASTM D-746 | <-80 | ℃ | |||