| 断裂伸长率 | 810% | 拉伸强度 | 42MPa | 密度 | 0.928g/cm3 |
| 熔体流动速率 | 2.8g/10min | 用途级别 | 薄膜级 | 规格级别 | 薄膜 |
| 缺口冲击强度 | 5 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
用途:制造伸直纸卷铸造薄膜而研制
备注:具有优秀的刚性延伸性、引张强度、无胶凝和加工性
备注:具有优秀的刚性延伸性、引张强度、无胶凝和加工性
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 2.8 | g/10min | ||
| 密度 | ASTM D-1505 | 0.928 | g/cm3 | |||
| 机械性能 | 撕裂强度 | MD | ASTM D-1004 | 8 | Kg/cm | |
| TD | ASTM D-1004 | 10 | Kg/cm | |||
| 伸长率 | MD | ASTM D-882 | 740 | % | ||
| TD | ASTM D-882 | 810 | % | |||
| 拉伸屈服强度 | MD | ASTM D-882 | 140 | Kg/cm2 | ||
| TD | ASTM D-882 | 140 | Kg/cm2 | |||
| 抗冲击强度 | ASTM D-3420 | 5 | Kg/cm | |||
| 拉伸断裂强度 | MD | ASTM D-882 | 460 | Kg/cm2 | ||
| TD | ASTM D-882 | 430 | Kg/cm2 | |||
| 撕裂弹性率 | MD | ASTM D-882 | 2800 | Kg/cm2 | ||
| TD | ASTM D-882 | 3300 | Kg/cm2 | |||
| 热性能 | 脆化温度 | ASTM D-746 | <-80 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 105 | ℃ | |||
| 其它性能 | 雾度 | ASTM D-1003 | 5 | % | ||
| 薄膜厚度 | ASTM D-746 | 30 | µm | |||