断裂伸长率 | 800% | 拉伸强度 | 26MPa | 密度 | 0.918g/cm3 |
熔体流动速率 | 2.8g/10min | 用途级别 | 薄膜级,光学级 | 规格级别 | 薄膜 |
缺口冲击强度 | 120 |
|
产品简述
断裂伸长率 | 800% | 拉伸强度 | 26MPa | 密度 | 0.918g/cm3 |
熔体流动速率 | 2.8g/10min | 用途级别 | 薄膜级,光学级 | 规格级别 | 薄膜 |
缺口冲击强度 | 120 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 2.8 | g/10min | |
密度 | ASTM D-1505 | 0.918 | g/cm3 | |||
屈服拉伸强度 | MD | ASTM D-882 | 13 | MPa | ||
TD | ASTM D-882 | 10 | MPa | |||
断裂拉伸强度 | MD | ASTM D-882 | 33 | MPa | ||
TD | ASTM D-882 | 26 | MPa | |||
机械性能 | 落镖冲击强度 | ASTM D-1709 | 120 | gf/50%F | ||
断裂伸长率 | MD | ASTM D-882 | 600 | % | ||
TD | ASTM D-882 | 800 | % | |||
埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 200 | g | ||
TD | ASTM D-1922 | 800 | g | |||
弹性模量 | MD | 1% | ASTM D-882 | 100 | MPa | |
TD | 1% | ASTM D-882 | 210 | MPa | ||
光学性能 | 雾度 | ASTM D-1003 | 1.7 | % | ||
光泽度 | 60° | ASTM D-2457 | 93 |