断裂伸长率 | 610% | 拉伸强度 | 12.4MPa | 密度 | 0.919g/cm3 |
熔体流动速率 | 1g/10min | 维卡软化点 | 104℃ | 规格级别 | 吹塑 |
加工级别 | 吹塑级,吹膜级 |
|
产品简述
断裂伸长率 | 610% | 拉伸强度 | 12.4MPa | 密度 | 0.919g/cm3 |
熔体流动速率 | 1g/10min | 维卡软化点 | 104℃ | 规格级别 | 吹塑 |
加工级别 | 吹塑级,吹膜级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
基本性能 | 比重 | ASTM D-792 | 0.919 | g/cm3 | ||||
熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min | ||||
机械性能 | 电影穿刺能源 | 20.3um | Internal Method | 4.63 | J | |||
电影穿刺能源 | 50.8um | Internal Method | 6.78 | J | ||||
电影穿刺力 | 20.3um | Internal Method | 53.4 | N | ||||
电影穿刺力 | 50.8um | Internal Method | 84.5 | N | ||||
电影穿刺抵抗 | 20.3um | Internal Method | 25.2 | J/cm3 | ||||
电影穿刺抵抗 | 50.8um | Internal Method | 17.9 | J/cm3 | ||||
电影韧性 | 20.3um | ASTM D-882 |
|
J/cm3 | ||||
电影韧性 | 50.8um | ASTM D-882 |
|
J/cm3 | ||||
割线模量-2% Secant | 20.3um | ASTM D-882 |
|
MPa | ||||
割线模量-2% Secant | 50.8um | ASTM D-882 |
|
MPa | ||||
拉伸屈服强度 | 20.3um | ASTM D-882 |
|
MPa | ||||
拉伸屈服强度 | 50.8um | ASTM D-882 |
|
MPa | ||||
拉伸断裂强度 | 20.3um | ASTM D-882 |
|
MPa | ||||
拉伸断裂强度 | 50.8um | ASTM D-882 |
|
MPa | ||||
拉伸断裂伸长率 | 20.3um | ASTM D-882 |
|
% | ||||
拉伸断裂伸长率 | 50.8um | ASTM D-882 |
|
% | ||||
落锤冲击 | 20.3um | ASTM D-1709A | 110 | g | ||||
落锤冲击 | 20.3um | ASTM D-1709B | <100 | g | ||||
落锤冲击 | 50.8um | ASTM D-1709A | 350 | g | ||||
落锤冲击 | 50.8um | ASTM D-1709B | 200 | g | ||||
埃尔曼多夫撕裂强度 | 20.3um | ASTM D-1922 |
|
g | ||||
埃尔曼多夫撕裂强度 | 50.8um | ASTM D-1922 |
|
g | ||||
密封起始温度 | 20.3um | Internal Method | 110 | ℃ | ||||
密封起始温度 | 50.8um | Internal Method | 120 | ℃ | ||||
密封强度 | 130℃,0.0203mm | Internal Method | 1000 | g | ||||
密封强度 | 150℃,0.0508mm | Internal Method | 2100 | g | ||||
加工性能 | 熔体温度 | 233 | ℃ | |||||
热性能 | 维卡软化点 | ASTM D-1525 | 104 | ℃ | ||||
熔化温度 | Internal Method | 124 | ℃ | |||||
光学性能 | 光泽度 | 20°,20.3um | ASTM D-2457 | 87 | ||||
光泽度 | 20°,50.8um | ASTM D-2457 | 64 | |||||
光泽度 | 45°,20.3um | ASTM D-2457 | 70 | |||||
光泽度 | 45°,50.8um | ASTM D-2457 | 59 | |||||
雾度 | 20.3um | ASTM D-1003 | 7 | % | ||||
雾度 | 50.8um | ASTM D-1003 | 14 | % |