| 断裂伸长率 | 600% | 拉伸强度 | 16.3MPa | 密度 | 0.926g/cm3 |
| 熔体流动速率 | 0.8g/10min | 维卡软化点 | 113℃ | 用途级别 | 薄膜级,光学级 |
| 规格级别 | 吹塑 | 加工级别 | 吹塑级 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
| 基本性能 | 比重 | ASTM D-792 | 0.926 | g/cm3 | ||||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.8 | g/10min | ||||
| 机械性能 | 电影穿刺能源 | 20.3um | Internal Method | 2.37 | J | |||
| 电影穿刺能源 | 50.8um | Internal Method | 5.42 | J | ||||
| 电影穿刺力 | 20.3um | Internal Method | 40 | N | ||||
| 电影穿刺力 | 50.8um | Internal Method | 80.1 | N | ||||
| 电影穿刺抵抗 | 20.3um | Internal Method | 14.2 | J/cm3 | ||||
| 电影穿刺抵抗 | 50.8um | Internal Method | 13.2 | J/cm3 | ||||
| 电影韧性 | 20.3um | ASTM D-882 |
|
J/cm3 | ||||
| 电影韧性 | 50.8um | ASTM D-882 |
|
J/cm3 | ||||
| 割线模量-2% Secant | 20.3um | ASTM D-882 |
|
MPa | ||||
| 割线模量-2% Secant | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸屈服强度 | 20.3um | ASTM D-882 |
|
MPa | ||||
| 拉伸屈服强度 | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸断裂强度 | 20.3um | ASTM D-882 |
|
MPa | ||||
| 拉伸断裂强度 | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸断裂伸长率 | 20.3um | ASTM D-882 |
|
% | ||||
| 拉伸断裂伸长率 | 50.8um | ASTM D-882 |
|
% | ||||
| 落锤冲击 | 20.3um | ASTM D-1709A | 58 | g | ||||
| 落锤冲击 | 20.3um | ASTM D-1709B | <100 | g | ||||
| 落锤冲击 | 50.8um | ASTM D-1709A | 190 | g | ||||
| 落锤冲击 | 50.8um | ASTM D-1709B | <100 | g | ||||
| 埃尔曼多夫撕裂强度 | 20.3um | ASTM D-1922 |
|
g | ||||
| 埃尔曼多夫撕裂强度 | 50.8um | ASTM D-1922 |
|
g | ||||
| 密封起始温度 | 20.3um | Internal Method | 120 | ℃ | ||||
| 密封起始温度 | 50.8um | Internal Method | 130 | ℃ | ||||
| 加工性能 | 熔体温度 | 234 | ℃ | |||||
| 热性能 | 维卡软化点 | ASTM D-1525 | 113 | ℃ | ||||
| 熔化温度 | Internal Method | 125 | ℃ | |||||
| 光学性能 | 光泽度 | 20°，20.3um | ASTM D-2457 | 66 | ||||
| 光泽度 | 20°，50.8um | ASTM D-2457 | 55 | |||||
| 光泽度 | 45°，20.3um | ASTM D-2457 | 56 | |||||
| 光泽度 | 45°，50.8um | ASTM D-2457 | 54 | |||||
| 雾度 | 20.3um | ASTM D-1003 | 9 | % | ||||
| 雾度 | 50.8um | ASTM D-1003 | 16 | % | ||||
| 密封强度 | 160℃，0.0203mm | Internal Method | 1300 | g | ||||
| 密封强度 | 180℃，0.0508mm | Internal Method | 2200 | g | ||||