加工级别 | 注塑级 |
|
产品简述
加工级别 | 注塑级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 密度 | ASTM D-792 | 0.927 | g/cm3 | |
熔体流动速率 | 190℃/2.16 kg | ASTM D-1238 | 4.5 | g/10min | |
厚度 | 50.8 | microns | |||
水汽传输 | ASTM F-372 | 4.3 | |||
机械性能 | 拉伸屈服强度 | MD | ASTM D-882 | 11.8 | MPa |
拉伸屈服强度 | TD | ASTM D-882 | 13.8 | MPa | |
埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 69 | g | |
埃尔曼多夫撕裂强度 | TD | ASTM D-1922 | 241 | g | |
断裂伸长率 | MD | ASTM D-882 | 780 | % | |
断裂伸长率 | TD | ASTM D-882 | 840 | % | |
屈服伸长率 | MD | ASTM D-882 | 12 | % | |
屈服伸长率 | TD | ASTM D-882 | 9 | % | |
拉伸断裂强度 | MD | ASTM D-882 | 22.9 | MPa | |
拉伸断裂强度 | TD | ASTM D-882 | 2.1 | MPa | |
热性能 | 维卡软化点 | ASTM D-1003 | 103 | ℃ | |
熔融温度 | 210 | ℃ | |||
爆破比(BUR) | 2 |