断裂伸长率 | 900% | 拉伸强度 | 36MPa | 密度 | 0.92g/cm3 |
熔体流动速率 | 2g/10min | 维卡软化点 | 102℃ | 用途级别 | 薄膜级 |
规格级别 | 薄膜 |
|
产品简述
断裂伸长率 | 900% | 拉伸强度 | 36MPa | 密度 | 0.92g/cm3 |
熔体流动速率 | 2g/10min | 维卡软化点 | 102℃ | 用途级别 | 薄膜级 |
规格级别 | 薄膜 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.920 | |||
熔体流动速率 | ASTM D-1238 | 2.0 | g/10min | |||
物理性能 | 薄膜厚度 | HPC | 40 | μm | ||
雾度 | ASTM D-1003 | 14 | % | |||
机械性能 | 断裂伸长率 | MD | ASTM D-882 | 780 | % | |
TD | ASTM D-882 | 900 | % | |||
拉伸强度 | TD | ASTM D-882 | 370 | kg/cm2 | ||
落球冲击强度 | ASTM D-1709A | 120 | g | |||
EL撕裂强度 | MD | ASTM D-1922 | 5.0 | g/μm | ||
TD | ASTM D-1922 | 9.0 | g/μm | |||
断裂点 | MD | ASTM D-882 | 400 | kg/cm2 | ||
热性能 | 维卡软化点 | ASTM D-1525 | 102 | ℃ |