加工级别 | 注塑级 | 特性级别 | 高抗冲 |
|
产品简述
加工级别 | 注塑级 | 特性级别 | 高抗冲 |
详细数据
订购指南
|
物理性质 | ||||
---|---|---|---|---|
比重 | ASTM D792 | Natural 或代表 color | - | 1.1 |
熔融指数 | ASTM D1238 | 220℃, 10kg | g/10min | 25 |
成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.3-0.4 |
成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.6 |
机械性质 | ||||
---|---|---|---|---|
拉伸强度(at yield) | ASTM D638 | 5mm/min | kgf/cm2 | 620 |
伸长率(at break) | ASTM D638 | 5mm/min | % | 12 |
拉伸模量 | ASTM D638 | 5mm/min | kgf/cm2 | 26000 |
断裂强度(at break) | ASTM D638 | 5mm/min | kgf/cm2 | 530 |
弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 950 |
弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 29000 |
Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 2 |
Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 2 |
Izod冲击强度(unnotched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 30 |
Izod冲击强度(unnotched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 30 |
硬度 | ASTM D785 | R-Scale | - | 118 |
铅笔硬度 | JIS K 5401 | 500g | - | 2H |
热学特性 | ||||
---|---|---|---|---|
热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 84 |
维卡软化温度 | ISO R 306 | B/50 | °C | 94 |
阻燃 | ||||
---|---|---|---|---|
阻燃度 | UL94 | HB | mm | 1.5~3.0 |