断裂伸长率 | 200% | 拉伸强度 | 63.72MPa | 密度 | 1.14g/cm3 |
吸水率 | 1.8% | 成型收缩率 | 1.2% | 特性级别 | 耐高温 |
|
产品简述
断裂伸长率 | 200% | 拉伸强度 | 63.72MPa | 密度 | 1.14g/cm3 |
吸水率 | 1.8% | 成型收缩率 | 1.2% | 特性级别 | 耐高温 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 成型收缩率 | UBEmethod | 1.3 | % | |
成型收缩率 | UBEmethod | 1.2 | % | ||
吸水率 | ASTM D-570 | 10.7 | % | ||
吸水率 | ASTM D-570 | 1.8 | % | ||
物理性能 | 比重 | ASTM D-792 | 1.14 | ||
机械性能 | 屈服下的伸张强度 | 23° | ASTM D-638 | 420 | kgf/cm2 |
弯曲弹性率 | 23° | ASTM D-790 | 8000 | kgf/cm2 | |
屈服下的伸张强度 | -30° | ASTM D-638 | 1100 | kgf/cm2 | |
挤剪强度 | 23° | ASTM D-732 | 650 | kgf/cm2 | |
屈服下的伸张强度 | -30° | ASTM D-638 | 9000 | kgf/cm2 | |
弯曲强度 | 80° | ASTM D-790 | 260 | kgf/cm2 | |
抗冲击强度 | 23° | ASTM D-256 | 50 | kgf.cm/cm | |
断裂下的伸张强度 | 23° | ASTM D-638 | 650 | kgf/cm2 | |
抗冲击强度 | -30° | ASTM D-256 | 4.5 | kgf.cm/cm | |
断裂下的延伸率 | 23° | ASTM D-638 | >200 | % | |
弯曲弹性率 | 80° | ASTM D-790 | 7500 | kgf/cm2 | |
屈服下的延伸率 | 23° | ASTM D-638 | 8 | % | |
屈服下的伸张强度 | 23° | ASTM D-638 | 800 | kgf/cm2 | |
断裂下的延伸率 | 23° | ASTM D-638 | 90 | % | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 85 | ||
TABER磨耗率 | ASTM D-1044 | 7 | mg | ||
弯曲强度 | -30° | ASTM D-790 | 1400 | kgf/cm2 | |
弯曲强度 | 23° | ASTM D-790 | 1100 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 120 | ||
1%变形下的压缩强度 | 23° | ASTM D-695 | 100 | kgf/cm2 | |
屈服下的伸张强度 | 80° | ASTM D-638 | 200 | kgf/cm2 | |
抗冲击强度 | 23° | ASTM D-256 | 6.5 | kgf.cm/cm | |
弯曲弹性率 | -30° | ASTM D-790 | 30500 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 55 | ||
弯曲强度 | -30° | ASTM D-790 | 1300 | kgf/cm2 | |
1%变形下的压缩强度 | 23° | ASTM D-695 | 200 | kgf/cm2 | |
弯曲弹性率 | -30° | ASTM D-790 | 32000 | kgf/cm2 | |
线性热膨胀系数 | ASTM D-696 | 8 | X的10-5cm/cm/°C | ||
屈服下的伸张强度 | 80° | ASTM D-638 | 320 | kgf/cm2 | |
弯曲强度 | 80° | ASTM D-790 | 500 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 85 | ||
弯曲强度 | 23° | ASTM D-790 | 400 | kgf/cm2 | |
挤剪强度 | 23° | ASTM D-732 | 600 | kgf/cm2 | |
弯曲弹性率 | 23° | ASTM D-790 | 29000 | kgf/cm2 | |
弯曲弹性率 | 80° | 4000 | |||
电气性能 | 体积电阻率 | ASTM D-257 | 1014 | Ω.cm | |
热性能 | 熔点 | DSC | 215-225 | °C | |
热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 180 | °C | |
燃烧率 | UL94 | V-2 |