详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 比重 | ASTM D792, ISO 1183 | 1.19 |
g/cm3;
|
|
收缩率 | 流动: 24小时 | ASTM D955 | 1.0--3.0 | % | |
横向流动: 24小时 | ASTM D955 | 1.0-3.0 | % | ||
机械性能 | 拉伸模量2 | |
ASTM D638 | 3730 | MPa |
抗张强度3 | 断裂 | ASTM D638 | 52.7 | MPa | |
伸长率3 |
断裂
|
ASTM D638 | 25 | % | |
弯曲模量4 |
|
ASTM D790 | 2150 | MPa | |
弯曲强度 | ASTM D790 | 78.0 | MPa | ||
摩擦系数 |
与自身 - 动态
|
ASTM D3702 Modified | 0.60 | ||
与自身 - 静态
|
ASTM D3702 Modified | 0.42 | |||
磨损因数 |
Ring
|
ASTM D3702 Modified | 0.300 |
10^-10 in^5-min/ft-lb-hr
|
|
Washer
|
ASTM D3702 Modified | 74.0 |
10^-10 in^5-min/ft-lb-hr
|
||
悬壁梁缺口冲击强度 | 23°C | ASTM D256 | 48 | J/m | |
23°C 5 |
ISO 180/1A | 4.9 | kJ/m2; | ||
无缺口悬臂梁冲击 | 23°C |
ASTM D4812 | 1200 | J/m | |
23°C 5 | ISO 180/1U | 68 | kJ/m2; | ||
装有测量仪表的落镖冲击 | 23°C, Energy at Peak Load | ASTM D3763 | 9.60 | J | |
-- | ISO 6603-2 | 24.7 | J | ||
热性能 | 热变形温度 |
0.45 MPa, 未退火, 3.20 mm
|
ASTM D648 | 144 | °C |
0.45 MPa, 未退火, 64.0 mm 跨距 6
|
ISO 75-2/Bf | 133 | °C | ||
1.8 MPa, 未退火, 3.20 mm
|
ASTM D648 | 54.0 | °C | ||
1.8 MPa, 未退火, 64.0 mm 跨距 6
|
ISO 75-2/Af | 51.0 | °C | ||
线形膨胀系数 |
流动: -30 到 30°C
|
ASTM D696 | 0.000096 | cm/cm/°C | |
横向: -30 到 30°C
|
ASTM D696 | 0.000095 | cm/cm/°C |