详细数据

订购指南

性能项目			试验条件[状态]	测试方法	测试数据	数据单位
物理性能	收缩率		平行流动方向	ASTM D955	0.016	cm/cm
物理性能	收缩率		垂直流动方向	ASTM D955	0.016	cm/cm
机械性能	弯曲模量		90 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant	ASTM D790	331	Mpa
	弯曲模量		（-40 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant	ASTM D790	3000	Mpa
	弯曲模量		23 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant	ASTM D790	2410	Mpa
	弯曲模量		149 °C, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant	ASTM D790	234	Mpa
	弯曲强度		90 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I	ASTM D790	13	Mpa
	弯曲强度		（-40 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I	ASTM D790	120	Mpa
	弯曲强度		23 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I	ASTM D790	80	Mpa
	弯曲强度		149 °C, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I	ASTM D790	8	Mpa
	断裂点伸长率	-	90 °C, 0.00 mm, Compression Molded, Type I	ASTM D638	300	%
		-	-40 °C, 0.00 mm, Compression Molded, Type I	ASTM D638	11	%
		-	23 °C, 0.00 mm, Compression Molded, Type I	ASTM D638	300	%
		-	150 °C, 0.00 mm, Compression Molded, Type I	ASTM D638	300	%
	非缺口冲击强度	-	-40 °C, 0.00 mm	ASTM D256	No Break	J/m
	非缺口冲击强度	-	23 °C, 0.00 mm	ASTM D256	No Break	J/m
热性能	熔点			DSC	225	℃
	阻燃性	-	3.00 mm	UL94	HB
		-	1.5mm	UL94	HB
		-	0.81mm	UL94	HB
其它性能	极限氧指数		3.20 mm	ASTM D2863	22	%

PBT/美国杜邦/6130C NC010 包装图片

产品导购

PVC/南通吉汇/6840

PA6/美国杜邦/7300T

PC/沙伯基础(原GE)/FXE124R

PA612/兰蒂奇美国/N612G43HSL

PCTG/伊斯曼化学/Z6020

牌号 :	6130C NC010
品牌 :	美国杜邦
种类 :	PBT
货期 :
价格 :	电询 13061808058

断裂伸长率	300%	弯曲强度	80MPa	规格级别	注塑
弯曲模量	2410MPa	成型收缩率	0.016%	阻燃等级	0
加工级别	注塑级	特性级别	增强级