详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 |
比重 | ASTM D792 | 1.37 |
g/cm3;
|
|
熔流率 | 230°C/2.16 kg | ASTM D1238 | 22 |
g/10 min
|
|
收缩率 | 流动 | ASTM D955 | 0.90 | % | |
吸水率 |
23°C, 24 hr
|
ASTM D570 | 0.050 | % | |
平衡, 23°C, 50% RH
|
ASTM D570 | 0.35 | % | ||
洛氏硬度 | M 计秤 | ASTM D785 | 90 | ||
拉伸模量 | ASTM D638 | 4400 |
MPa
|
||
抗张强度 |
极限
|
ASTM D638 | 80.0 |
MPa
|
|
伸长率 | 断裂 | ASTM D638 | 3.5 | % | |
弯曲模量 | ASTM D790 | 3500 |
MPa
|
||
弯曲强度 | ASTM D790 | 140 |
MPa
|
||
简支梁缺口冲击强度 | 23°C) | ISO 179 | 7.0 |
kJ/m2;
|
|
简支梁缺口冲击强度 |
-30°C
|
ISO 179 | 25 | kJ/m2; | |
23°C
|
ISO 179 | 30 | kJ/m2; | ||
悬壁梁缺口冲击强度 | 23°C | ASTM D256A | 35 |
J/m
|
|
热性能 | 热变形温度 |
0.45 MPa, 未退火
|
ASTM D648 | 215 |
°C
|
1.8 MPa, 未退火
|
ASTM D648 | 200 |
°C
|
||
维卡软化温度 | ASTM D1525 | 205 |
°C
|
||
线形膨胀系数 | 流动 | ASTM D696 | 0.000050 |
cm/cm/°C
|
|
电气性能 |
表面电阻率 | ASTM D257 |
1.0E+14
|
ohms
|
|
体积电阻率 | ASTM D257 |
1.0E+15
|
ohm·cm
|
||
介电强度 | 1.60 mm | ASTM D149 | 20 |
kV/mm
|
|
介电常数 | 1 kHz | ASTM D150 | 3.50 | ||
耗散因数 | 1 kHz | ASTM D150 | 0.0020 | ||
漏电起痕指数 | IEC 60112 | 350 |
V
|
||
可燃性 | UL 阻燃等级 | 0.800 mm | UL 94 |
HB
|